A Damage Accumulating Modeling of Failure Waves in Glass under High Velocity Impact

LIU Zhan-fang; YAO Guo-wen; ZHAN Xian-yi

Article Contents

Article Navigation > Applied Mathematics and Mechanics > 2001 > 22(9): 983-987

LIU Zhan-fang, YAO Guo-wen, ZHAN Xian-yi. A Damage Accumulating Modeling of Failure Waves in Glass under High Velocity Impact[J]. Applied Mathematics and Mechanics, 2001, 22(9): 983-987.

Citation:

LIU Zhan-fang, YAO Guo-wen, ZHAN Xian-yi. A Damage Accumulating Modeling of Failure Waves in Glass under High Velocity Impact[J]. Applied Mathematics and Mechanics, 2001, 22(9): 983-987.

Citation:

LIU Zhan-fang, YAO Guo-wen, ZHAN Xian-yi. A Damage Accumulating Modeling of Failure Waves in Glass under High Velocity Impact[J]. Applied Mathematics and Mechanics, 2001, 22(9): 983-987.

PDF( 226 KB)

A Damage Accumulating Modeling of Failure Waves in Glass under High Velocity Impact

Department of Engineering Mechanics, Chongqing University, Chongqing 400044, P R China

Received Date: 2000-09-25
Rev Recd Date: 2001-04-08
Publish Date: 2001-09-15

Abstract

Abstract

The failure wave phenomenon was interpreted in glassmedia under the high velocity impact with the stress levels below the Hugoniot elastic limit. Inview of the plate impact experimental observations a damage-accumulating model predominated by the deviatoric stress impulse was proposed while Heaviside function was adopted in the damage-accumulating model to describe the failure delay inthe interior of materials. Features of the failure layer and propagation mechanism as well as their dynamic characteristics were further presented. The reduction in failure wave propagation speed is pointed out as the reflected rarefaction waves reflect again from the failure layer boundary.
- high velocity impact,
- failure wave,
- damage-accumulating model

FullText(HTML)

References(10)

References

[1]	Rasorenov S V, Kanel G I, Fortov V E, et al. The fracture of glass under high-pressure impulsive loading[J]. High Pressure Research,1991,6:225-232.
[2]	Partom Y. Modeling failure waves in glass[J]. Int J Impact Engng,1998,21(9):791-799.
[3]	Espinosa H D, Xu Y P. Micromechanics of failure waves in glass: Ⅰ Experiments[J]. J Am Ceram Soc,1997,80(8):2061-2073.
[4]	Espinosa H D, Xu Y P. Micromechanics of failure waves in glass: Ⅱ Modeling[J]. J Am Ceram Soc,1997,80(8):2074-2085.
[5]	Clifton R J. Analysis of failure waves in glasses[J]. Appl Mech Rev,1993,46(12):540-546.
[6]	HE Hong-liang, JING Fu-qian, JIN Xiao-gang, et al. Compressive failure of brittle materials under shock wave loading[A]. In: Sino-Japanese Symp Deformation/Fracture of Solids[C]. Huangshan/China,1997,81-90.
[7]	HE Hong-liang. Dynamic response and microstructure damage of brittle materials under shock wave compression[D]. Ph D Thesis. Chengdu: Institute of Fluid Physics, CAEP, 1997.
[8]	经福谦. 实验物态方程导引[M]. 北京:科学出版社,1986.
[9]	王礼立. 应力波基础[M]. 北京:国防工业出版社,1985.
[10]	高蕴昕,郑泉水,余寿文. 各向同性弹性损伤的的双标量描述[J]. 力学学报,1996,28(5):542-549.